Amorphous metal

An amorphous metal (also known as metallic glass, glassy metal, or shiny metal) is a solid metallic material, usually an alloy, with disordered atomic-scale structure. Most metals are crystalline in their solid state, which means they have a highly ordered arrangement of atoms. Amorphous metals are non-crystalline, and have a glass-like structure. But unlike common glasses, such as window glass, which are typically electrical insulators, amorphous metals have good electrical conductivity and can show metallic luster. There are several ways in which amorphous metals can be produced, including extremely rapid cooling, physical vapor deposition, solid-state reaction, ion irradiation, and mechanical alloying. Previously, small batches of amorphous metals had been produced through a variety of quick-cooling methods, such as amorphous metal ribbons which had been produced by sputtering molten metal onto a spinning metal disk (melt spinning). The rapid cooling (in the order of millions of degrees Celsius a second) is too fast for crystals to form and the material is "locked" in a glassy state. Currently, a number of alloys with critical cooling rates low enough to allow formation of amorphous structure in thick layers (over ) have been produced; these are known as bulk metallic glasses. More recently, batches of amorphous steel with three times the strength of conventional steel alloys have been produced. The first reported metallic glass was an alloy (Au75Si25) produced at Caltech by W. Klement (Jr.), Willens and Duwez in 1960. This and other early glass-forming alloys had to be cooled extremely rapidly (on the order of one megakelvin per second, 106 K/s) to avoid crystallization. An important consequence of this was that metallic glasses could only be produced in a limited number of forms (typically ribbons, foils, or wires) in which one dimension was small so that heat could be extracted quickly enough to achieve the necessary cooling rate. As a result, metallic glass specimens (with a few exceptions) were limited to thicknesses of less than one hundred micrometers.