The large-area synthesis of high-quality MoS2 plays an important role in realizing industrial applications of optoelectronics, nanoelectronics, and flexible devices. However, current techniques for chemical vapor deposition (CVD)-grown MoS2 require a high synthetic temperature and a transfer process, which limits its utilization in device fabrications. Here, the direct synthesis of high-quality monolayer MoS2 with the domain size up to 120 mu m by metal-organic CVD (MOCVD) at a temperature of 320 degrees C is reported. Owing to the low-substrate temperature, the MOCVD-grown MoS2 exhibits low impurity doping and nearly unstrained properties on the growth substrate, demonstrating enhanced electronic performance with high electron mobility of 68.3 cm(2) V-1 s(-1) at room temperature. In addition, by tuning the precursor ratio, a better understanding of the MoS2 growth process via a geometric model of the MoS2 flake shape, is developed, which can provide further guidance for the synthesis of 2D materials.