Films minces relaxeur-ferroélectriques à base de Pb(Mg1/3NB2/3)O3 : élaboration, propriétés diélectriques et électromécaniques

Relaxor Pb(Mg1/3Nb2/3)O3(PMN) and its solid solutions with ferroelectric PbTiO3 (PT) are of considerable interest from both the applications and the scientific point of view. In the past, many attempts were made to prepare and study the properties of these material in thin film form. However, due to difficulties in the preparation of pure phase films with high PMN content, there exists very little knowledge on the properties of these important materials. It is the goal of this thesis to prepare PMN and PMN-PT films without second any phases, to study in detail their structure, dielectric and electromechanical properties, and to see how these properties compare with those of the bulk materials. The studies were carried out along three major directions: PMN, 0.9PMN-0.1PT and PT chemical solution precursor syntheses, thin films preparation, dielectric and electromechanical properties characterization and their interpretation. The synthesis of precursors used for the preparation of PMN, 0.9PMN-0.1PT and PT films is reported in detail. Careful control and optimization of the precursors was important to obtain thin films without second any phases. The presence of new compounds and reaction mechanisms were established in the course of developing reproducible and stable precursors solutions. Crystallization of pure PMN and 09PMN-0.1PT films requires high temperatures (∼800°C) and lead excess in the precursor solutions making processing difficult. The correct choice of seeding layers that favor perovskite phase nucleation and growth minimizing substrate instabilities at high temperatures was essential. This approach allowed us to find a narrow processing window that lead to films without pyrochlore and other second any phases. Important PMN and 09PMN-0.1PT processing parameters are reported. It is shown that crystallographic orientation and microstructure could be modified by controlling the perovskite phase nucleation and growth with different seeding layers (TiO2 and PbTiO3). PMN film epitaxial growth on conductive SrTiO3 single crystals allowed an original transmission electron microscopy study. The results showed that PMN in thin film and bulk forms shows the same structural characteristics (morphology and size of polar regions). However, temperature dependence of unit cell parameters of PMN and 09PMN-0.1PT films seems to be qualitatively different from these obtained in bulk materials. PMN and 0.9PMN-0.1PT thin films show typical relaxor characteristics (dielectric permittivity dependence on frequency and temperature, presence of polar regions, superstructure, ferroelectric hysteresis at low temperature) however significant differences exist between films and bulk materials. Most of these differences (low permittivity, presence of the self-polarization) are at least in part related to the properties of the substrate used, as well as the conditions of films preparation. The presented results clearly show the influence of the measuring signal and proce