DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
Iron-based shape memory alloys (Fe-SMAs) can be used for strengthening of existing concrete structures in civil and architectural engineering. This study investigates the recovery behavior of Fe-SMAs under varying pre-strain levels, activation temperatures, and thermos-mechanical training conditions. An FeMnSi-based alloy (Fe-17Mn-10Cr-5Si-4Ni-0.2C-0.8V wt.%) underwent two-step aging, followed by pre-straining at 2 %, 4 %, and 8 % and activation at 200 degrees C, 400 degrees C, and 600 degrees C. Recovery stresses under rigid restraint reached 500 MPa, 490 MPa, and 440 MPa at 200 degrees C for 2 %, 4 %, and 8 % pre-strain, respectively, while at 8 % pre-strain and 600 degrees C, recovery stress exceeded 600 MPa. Free-recovery strains for 8 % pre-strain were 1 %, 2 %, and 2.15 % at 200 degrees C, 400 degrees C, and 600 degrees C, respectively. Thermomechanical training involving 10 cycles of 3 % pre-strain and annealing at 400 degrees C and 600 degrees C increased the shape recovery ratio to 95 %. Microstructural analysis showed reduced twin boundary density, enhancing the epsilon-martensite to gamma-austenite transformation and improving recovery performance after training. Optimal pre-strain levels, activation temperatures, heat treatment, and thermomechanical training significantly improved the shape memory effect (SME) and super elasticity (SE) of Fe-SMAs. Key findings demonstrate that: (1) activation at 350 degrees C-600 degrees C maximized recovery stress and strain, with diminishing returns at excessively high temperatures; (2) thermomechanical training enhanced SME and SE via work hardening and increased dislocation density; and (3) microstructural refinement through annealing improved recovery ratios, with optimal performance achieved at 600 degrees C. These results provide valuable insights into tailoring the recovery behavior of Fe-SMAs for advanced applications.