Tensile Test and Deformation Analysis

Graph Chat

Chat with Graph Search

Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.

DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.

In course

MSE-310: Deformation of materials

Présentation des mécanismes de déformation des matériaux inorganiques: élasticité, plasticité, fluage. ...

Description

This lecture covers the principles of tensile testing, including necking, ductility, and work hardening. It also delves into the analysis of deformation, true constraints, and the influence of factors like temperature and grain size. The instructor discusses the importance of understanding true deformation and constraints in material testing.

Instructor

Roland Logé

Roland Logé is an associate professor at EPFL, with a primary affiliation to the Materials Institute, and a secondary affiliation to the Microengineering Institute. After graduating in 1994 at UCL (Belgium) in Materials Engineering, he earned a Master of Science in Mechanics in 1995, at UCSB Santa Barbara (USA). He received his PhD at Mines Paristech-CEMEF (France) in 1999, where he specialized in metal forming and associated microstructure evolutions. After a postdoc at Cornell University (USA) between 1999 and 2001, he entered CNRS in France. In 2008, he was awarded the ALCAN prize from the French Academy of Sciences, together with Yvan Chastel. In 2009 he became head of the Metallurgy-Structure-Rheology research group at CEMEF. In 2011, he launched a “Groupement de Recherche” (GDR), funded by CNRS, networking most of the researchers in France involved in recrystallization and grain growth. In 2013, he became Research Director at CNRS. In March 2014 he joined EPFL as the head of the Laboratory of Thermomechanical Metallurgy.

Official source

Ontological neighbourhood

Chemical engineering

Materials science: Deformation of materials

Related concepts (32)

Work hardening

In materials science, work hardening, also known as strain hardening, is the strengthening of a metal or polymer by plastic deformation. Work hardening may be desirable, undesirable, or inconsequential, depending on the context. This strengthening occurs because of dislocation movements and dislocation generation within the crystal structure of the material. Many non-brittle metals with a reasonably high melting point as well as several polymers can be strengthened in this fashion.

Tensile testing

Tensile testing, also known as tension testing, is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength, breaking strength, maximum elongation and reduction in area. From these measurements the following properties can also be determined: Young's modulus, Poisson's ratio, yield strength, and strain-hardening characteristics.

Ductility

Ductility is a mechanical property commonly described as a material's amenability to drawing (e.g. into wire). In materials science, ductility is defined by the degree to which a material can sustain plastic deformation under tensile stress before failure. Ductility is an important consideration in engineering and manufacturing. It defines a material's suitability for certain manufacturing operations (such as cold working) and its capacity to absorb mechanical overload.

Deformation (engineering)

In engineering, deformation refers to the change in size or shape of an object. Displacements are the absolute change in position of a point on the object. Deflection is the relative change in external displacements on an object. Strain is the relative internal change in shape of an infinitesimally small cube of material and can be expressed as a non-dimensional change in length or angle of distortion of the cube. Strains are related to the forces acting on the cube, which are known as stress, by a stress-strain curve.

Hardenability

Hardenability is the depth to which a steel is hardened after putting it through a heat treatment process. It should not be confused with hardness, which is a measure of a sample's resistance to indentation or scratching. It is an important property for welding, since it is inversely proportional to weldability, that is, the ease of welding a material. When a hot steel work-piece is quenched, the area in contact with the water immediately cools and its temperature equilibrates with the quenching medium.

Related lectures (64)

Mechanical Properties and Deformation Analysis

Explores mechanical properties, deformation analysis, and material behavior under various conditions, emphasizing the trade-off between hardness and ductility.

Plastic Deformation: Compression and Hardness Testing

Explores plastic deformation in compression testing, friction effects, hardness testing techniques, crystal defects, and micro-hardness tests.

Lamination: Deformation, Ductility, and Dislocations

Explores lamination, ductility, plastic deformation, and dislocations in materials, emphasizing the effects of strain rate and temperature.

Dislocations and Deformation

Explores dislocations in crystals, deformation mechanisms, and the effects of obstacles on dislocation movement.