AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.
We report pressure-induced metallization in BaMn 2 P 2 based on resistivity measurements in a diamond anvil cell. At ambient pressure, the temperature-dependent resistivity is well described by a two-gap Arrhenius model, yielding intrinsic and extrinsic activation energies of approximately 0.2 and 0.04 eV, respectively. Angle-resolved photoemission spectroscopy (ARPES) shows no detectable spectral weight at the Fermi level within the measured momentum window. The growth of spectral weight at higher binding energies is consistent with the energy scales inferred from transport measurements. Under pressure, the temperature dependence of the resistivity evolves from insulatinglike to mixed-slope behavior and becomes metallic above P c ≈ 7 GPa , with no low-temperature upturn. The resistivity ratio R ( P ) = ρ ( 100 K ) / ρ ( 300 K ) also drops abruptly near P c . A baseline transport model combining Bloch-Grüneisen phonon scattering with a thermally activated carrier density fails to reproduce this sharp change for any smoothly varying activation energy. Temperature- and pressure-dependent x-ray diffraction shows smooth evolution of V with no symmetry change and no resolvable discontinuity at P c . Taken together, these results indicate an abrupt pressure-driven metallization near P c , with no evidence for a structural phase transition within our experimental resolution.
Giorgio Margaritondo, László Forró, Marco Grioni, Luca Perfetti