Nucleation and growth of supported clusters at defect sites: Pd/MgO(001)

Klaus Kern, Harald Brune
2000
Journal Articles

Résumé

Nucleation and growth of Pd on cleaved MgO(001) surfaces were studied by variable-temperature atomic force microscopy in the temperature range 200-800 K. Constant island densities (similar to 3x10(12)cm(-2)) were observed over a wide temperature range, indicating nucleation kinetics governed by point defects with a high trapping energy. These results are compared to a rate equation model that describes the principal atomistic nucleation and growth processes, including nucleation at attractive point defects. Energies for defect trapping, adsorption, surface diffusion, and pair binding are deduced, and compared with recent nb initio calculations.

Source officielle

https://infoscience.epfl.ch/entities/publication/dc09baeb-f7ff-4d5e-8819-f94271887bff

À propos de ce résultat

Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Graph Chat

Chattez avec Graph Search

Posez n’importe quelle question sur les cours, conférences, exercices, recherches, actualités, etc. de l’EPFL ou essayez les exemples de questions ci-dessous.

AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.

Klaus Kern, Harald Brune
2000
Journal Articles

Résumé

Source officielle

https://infoscience.epfl.ch/entities/publication/dc09baeb-f7ff-4d5e-8819-f94271887bff

À propos de ce résultat

Concepts associés (32)

Schottky defect

A Schottky defect is an excitation of the site occupations in a crystal lattice leading to point defects named after Walter H. Schottky. In ionic crystals, this defect forms when oppositely charged ions leave their lattice sites and become incorporated for instance at the surface, creating oppositely charged vacancies. These vacancies are formed in stoichiometric units, to maintain an overall neutral charge in the ionic solid. Schottky defects consist of unoccupied anion and cation sites in a stoichiometric ratio.

Self-assembly of nanoparticles

Nanoparticles are classified as having at least one of three dimensions be in the range of 1-100 nm. The small size of nanoparticles allows them to have unique characteristics which may not be possible on the macro-scale. Self-assembly is the spontaneous organization of smaller subunits to form larger, well-organized patterns. For nanoparticles, this spontaneous assembly is a consequence of interactions between the particles aimed at achieving a thermodynamic equilibrium and reducing the system’s free energy.

Défaut ponctuel

En cristallographie, les défauts ponctuels sont des défauts dans l'organisation des cristaux qui ne concernent que des nœuds isolés. Le cristal parfait est un empilement régulier et infini d'atomes, ions ou molécules. Considérons le cas simple d'un cristal atomique ou ionique. Un défaut ponctuel typique est l'absence d'un atome (lacune), la présence d'un atome du réseau entre les atomes (défaut interstitiel), la présence d'un atome étranger entre les atomes du réseau (solution solide interstitielle) ou à la place d'un atome du réseau (solution solide de substitution).

Afficher plus

Publications associées (10)

Afficher plus

Nucleation and growth of supported clusters at defect sites: Pd/MgO(001)

Chattez avec Graph Search

Catalyst and Electrode Design for Selective and Durable Copper-Catalyzed Electrochemical Carbon Dioxide Reduction

Implantation and electron emission in cluster-surface collisions

Electrochemical characterisation of oxygen nonstoichiometry and transport in mixed conducting oxides : Application to La0.4Ba0.6Fe0.8Co0.2O3