Thermoelectrics converting heat and electricity directly attract broad attentions. To enhance the thermoelectric figure of merit, zT, one of the key points is to decouple the carrier-phonon transport. Here, we propose an entropy engineering strategy to realize the carrier-phonon decoupling in the typical SrTiO3-based perovskite thermoelectrics. By high-entropy design, the lattice thermal conductivity could be reduced nearly to the amorphous limit, 1.25 W m−1 K−1. Simultaneously, entropy engineering can tune the Ti displacement, improving the weighted mobility to 65 cm2 V−1 s−1. Such carrier-phonon decoupling behaviors enable the greatly enhanced μW/κL of ~5.2 × 103 cm3 K J−1 V−1. The measured maximum zT of 0.24 at 488 K and the estimated zT of ~0.8 at 1173 K in (Sr0.2Ba0.2Ca0.2Pb0.2La0.2)TiO3 film are among the best of n-type thermoelectric oxides. These results reveal that the entropy engineering may be a promising strategy to decouple the carrier-phonon transport and achieve higher zT in thermoelectrics.