Properties of thin layers of Sn62Pb36Ag2

Ludger Weber
1995
Conference Papers

Résumé

There is some confusion in the literature about the material parameters for eutectic tin-lead solder. This is mainly caused by the varying parameters under which the samples are processed and treated prior to testing, which lead to different microstructures. For instance, most investigations are performed with bulk material, some with thin layers. However, the thickness of these layers measures over 100μm; and it is not known whether the material parameters determined on 100μm specimens are appropriate for solder layers of 30μm. This study focuses on the determination of the deformation behavior of thin layers, down to 25μm, of Sn62Pb36Ag2.

Source officielle

https://infoscience.epfl.ch/entities/publication/b6b0b3cd-ebd0-4568-963f-66f48e68994c

À propos de ce résultat

Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Graph Chat

Chattez avec Graph Search

Posez n’importe quelle question sur les cours, conférences, exercices, recherches, actualités, etc. de l’EPFL ou essayez les exemples de questions ci-dessous.

AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.

Ludger Weber
1995
Conference Papers

Résumé

Source officielle

https://infoscience.epfl.ch/entities/publication/b6b0b3cd-ebd0-4568-963f-66f48e68994c

À propos de ce résultat

Concepts associés (23)

Solder

Solder (UKˈsɒldə,_ˈsəʊldə; NA: ˈsɒdər) is a fusible metal alloy used to create a permanent bond between metal workpieces. Solder is melted in order to wet the parts of the joint, where it adheres to and connects the pieces after cooling. Metals or alloys suitable for use as solder should have a lower melting point than the pieces to be joined. The solder should also be resistant to oxidative and corrosive effects that would degrade the joint over time. Solder used in making electrical connections also needs to have favorable electrical characteristics.

Brasage

thumb|Brasage de composants électroniques. Le brasage des métaux, aussi appelé brasure, est un procédé d'assemblage permanent qui établit une liaison métallique entre les pièces réunies. Contrairement au soudage (soudure), il n'y a pas fusion des bords assemblés. Selon les cas, il peut y avoir ou non utilisation d'un . Le mécanisme du brasage consiste en la diffusion/migration atomique de part et d'autre de l'interface solide/solide dans le cas d'un brasage sans métal d'apport et de l'interface solide/liquide/solide lorsqu'un métal d'apport est utilisé.

Résistance des matériaux

vignette|Essai de compression sur une éprouvette de béton, une pression croissante est appliquée verticalement sur l'échantillon pendant que deux appareils mesurent les déformations longitudinales et transversales de l'éprouvette. vignette|À l'issue du test, l'éprouvette s'est rompue. Notez la cassure longitudinale. La résistance des matériaux (RDM) est une discipline particulière de la mécanique des milieux continus, permettant le calcul des contraintes et déformations dans les structures des différents matériaux (machines, génie mécanique, bâtiment et génie civil).

Afficher plus

Publications associées (9)

Afficher plus

Properties of thin layers of Sn62Pb36Ag2

Chattez avec Graph Search

Cryogenic micropillar compression of Ti3AlC2, Ti3SiC2 and Cr2AlC: A comparative evaluation of composition-dependent dislocation mobility in MAX Phases

X-ray tomography analysis of particle morphology influence on granular deformation processes

How does seismic anisotropy evolve as a function of mineralogical and textural changes across ductile shear zones? – an experimental and modelling approach