The authors have studied InxGa1-xN/GaN (x approximate to 15%) quantum wells (QWs) using atomic force microscopy (AFM) and picosecond time resolved cathodoluminescence (pTRCL) measurements. They observed a contrast inversion between monochromatic CL maps corresponding to the high energy side (3.13 eV) and the low energy side (3.07 eV) of the QW luminescence peak. In perfect correlation with CL images, AFM images clearly show regions where the QW thickness almost decreases to zero. Pronounced spectral diffusion from high energy thinner regions to low energy thicker regions is observed in pTRCL, providing a possible explanation for the hindering of nonradiative recombination at dislocations. (c) 2006 American Institute of Physics.