Alternative anode materials for methane oxidation in solid oxide fuel cells

Fuel Cells are electrochemical devices that are able to directly convert chemical energy to electrical energy, without any Carnot limitation. Hence, their energy efficiencies are relatively high. Among the various types of fuel cells, solid oxide fuel cells (SOFC) are operated at high temperatures and in principle can run on various fuels such as natural gas and hydrogen. As natural gas is sought to become one of the main fuels of the next decades, its direct feed to a SOFC is desirable as the reaction free energy is high CH4 + 2O2 = CO2 + 2H2O, ΔrG°800°C = -800.8kJ/mol At present, conventional SOFC are operated with pure hydrogen or partially to fully reformed natural gas implying an efficiency penalty. SOFC anodes are generally made of electrocatalytically active Ni-YSZ cermet. Pure CH4 is not fed directly to the anode, because of problems associated with the anode deactivation and coking as CH4 leads to the detachment of Ni particles from the YSZ support and their encapsulation by carbon. To overcome this problem, partially oxidized or reformed CH4 is used. For SOFCs running on direct CH4 feed, alternative anode materials to Ni-YSZ, or new anode formulations are necessary. However, in this case, several parameters influence the anode performance and stability. The anodes should withstand reduction at a low PO2 of around 10-24 atm, be compatible with the SOFC electrolyte, possess an acceptable conductivity and thermal expansion coefficient, and appropriate catalytic and electrocatalytic properties along with low coking activity. LaCrO3 and CeO2-based materials as well as some metal catalysts were studied here for their potential application as anodes in direct oxidation of CH4. This choice of materials was made as lanthanum chromite and ceria-based materials are mixed conductors known to resist quite well to the very reducing conditions in SOFC as they are commonly used for interconnect and electrolyte materials respectively. Moreover, these compounds possess some catalytic activity for CH4 activation and combustion. LaCrO3 and CeO2-based materials show rather low electrical conductivity (on the order of 1 S/cm in reducing conditions), necessitating the application of an extra material for proper current collection. Nevertheless, these oxides possess many of the stringent characteristics cited above. For SOFC anode purposes, LaCrO3-based compounds, substituted with Ca, Sr, Mg, Mn, Fe, Co and Ni, were synthesized by a modified citrate route from nitrate precursors. An optimal calcination temperature of 1100°C was found to be necessary to obtain XRD-pure yet sinteractive compounds. Conductivity measurements in air and in reducing atmospheres of 10-21 atm showed that the La A-site substituents (Ca and Sr) influenced the conductivity more than the Cr B-site substituents (Mg, Mn, Fe, Co and Ni). In humidifed H2, the total conductivity was maximally of 6.5 S/cm. Surface reaction with YSZ electrolyte was evidenced by SEM, XPS and SIMS, in reducing con