Tensile properties and microstructure of 590 MeV proton-irradiated pure Fe and a Fe-Cr alloy

Maximo Pedro Victoria, Robin Schäublin
2000
Journal Articles

Résumé

Polycrystalline pure Fe and Fe-12Cr alloy have been proton-irradiated to doses of 10(-3)-3 x 10(-1) dpa at room temperature and 523 K. Samples were mechanically tested in tension and transmission electron microscopy (TEM) was performed on the as-irradiated material as well as on the irradiated and deformed material. At room temperature, pure Fe presents an initial yield point, that increases with the dose, followed by a yield region, indicative of a localized deformation mode. The Fe-12Cr alloy shows the same behavior, but the irradiation amplifies the effects previously mentioned. No yield point or yield region appears after irradiation at 523 K. TEM observations of the irradiated material showed a high density of small defect clusters which increases with the dose. Defect-free channels are observed in Fe-12Cr irradiated and deformed at room temperature. Results of the present investigation are compared with neutron irradiation of similar materials. (C) 2000 Elsevier Science B.V. All rights reserved.

Source officielle

https://infoscience.epfl.ch/entities/publication/03f76c30-bfbd-4f45-9016-d369700f1e2e

À propos de ce résultat

Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Graph Chat

Chattez avec Graph Search

Posez n’importe quelle question sur les cours, conférences, exercices, recherches, actualités, etc. de l’EPFL ou essayez les exemples de questions ci-dessous.

AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.

Maximo Pedro Victoria, Robin Schäublin
2000
Journal Articles

Résumé

Source officielle

https://infoscience.epfl.ch/entities/publication/03f76c30-bfbd-4f45-9016-d369700f1e2e

À propos de ce résultat

Concepts associés (32)

Superalliage

Un superalliage ou alliage à haute performance est un alliage métallique présentant une excellente résistance mécanique et une bonne résistance au fluage à haute température (typiquement sa température de fusion), une bonne stabilité surfacique ainsi qu'une bonne résistance à la corrosion et à l'oxydation. Les superalliages présentent typiquement une structure cristalline cubique à faces centrées de type austénitique. Les éléments d'alliages à la base d'un superalliage sont le plus souvent le nickel, le cobalt et le fer, mais aussi le titane et l'aluminium.

Yield (engineering)

In materials science and engineering, the yield point is the point on a stress-strain curve that indicates the limit of elastic behavior and the beginning of plastic behavior. Below the yield point, a material will deform elastically and will return to its original shape when the applied stress is removed. Once the yield point is passed, some fraction of the deformation will be permanent and non-reversible and is known as plastic deformation.

Aluminium alloy

An aluminium alloy (or aluminum alloy; see spelling differences) is an alloy in which aluminium (Al) is the predominant metal. The typical alloying elements are copper, magnesium, manganese, silicon, tin, nickel and zinc. There are two principal classifications, namely casting alloys and wrought alloys, both of which are further subdivided into the categories heat-treatable and non-heat-treatable. About 85% of aluminium is used for wrought products, for example rolled plate, foils and extrusions.

Afficher plus

Publications associées (32)

Afficher plus

Tensile properties and microstructure of 590 MeV proton-irradiated pure Fe and a Fe-Cr alloy

Chattez avec Graph Search

Modelling Masonry Arches Using Rigid Block Programming within the OpenSees Framework

Microscale analysis of hydraulically created fractures in sandstone

Effects of pore fluid chemistry on localised and ductile deformation of porous rocks