AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.

Laminated composites are prone to fracture at layer interfaces. Such damage impairs their structural response and engenders important constraints in design. In this work, the influence of ply orientation on crack growth resistance was studied for three dif ...

Fiber reinforced polymers (FRPs) subjected to mode I fracture show important toughening due to the development of large scale bridging (LSB). Experimental studies of this phenomenon in unidirectional carbon/epoxy laminates using double cantilever beam spec ...

Layered fiber reinforced composite materials are prone to fracture in planes parallel to the direction of fibers leading to extensive delamination or intralaminar fracture. This phenomenon of crack propagation is frequently accompanied by significant incre ...

Traction-separation relations due to large scale bridging in composites are very important in modeling their fracture response. Several works demonstrated that such relations are dependent upon the specimen's stiffness and loading conditions. Experimental ...

Combining additive manufacturing (AM) with carbon fiber reinforced polymer patched composites unlocks potentials in the design of individualized, lightweight biomedical structures. Arising design opportunities are geometrical individualization of structure ...

Post-disruption runaway electron (RE) beams in tokamaks with large current can cause deep melting of the vessel and are one of the major concerns for ITER operations. Consequently, a considerable effort is provided by the scientific community in order to t ...

This article reports modeling techniques and results based on experimental Mode I characterization of a layered woven GFRP material with tufting reinforcement. Standard tuft and loop-less geometries are investigated on three different areal patterns to eva ...

Delamination is a very frequent damage mechanism that affects the integrity of laminated composites. In this study, the effect of ply orientation on crack growth resistance was analyzed for three different anti-symmetric interfaces (+/- 30 degrees, +/- 45 ...

The mode I delamination behavior of a unidirectional glass-fiber reinforced polymer with a prototype elasto-plastic polyurethane matrix (GF/PU) was investigated and compared with that of glass/epoxy (GF/EP) using double cantilever beam specimens. Fracture ...

This experimental study reports effect of tuft geometry i.e., standard tufts and loops milled-down, and tufting pattern on Mode I interlaminar fracture in a GFRP. Standard tufting geometry is responsible for an increase in fracture resistance by 3.5-6 time ...

In this work the differences in R-curve response and traction-separation relations due to a finite damage zone or large-scale bridging (LSB) in mode I fracture on double cantilever beams (DCB) were investigated under end opening forces (EOF) and pure momen ...

In this study, silica glass, optical fiber Bragg gratings (FBGs) are used for torque-induced strain monitoring in carbon fiber reinforced polymer (CFRP) hollow shafts toward the development of a methodology for structural load monitoring. Optical fibers wi ...

Georgios Pappas

Chattez avec Graph Search

Influence of ply-angle on fracture in antisymmetric interfaces of CFRP laminates

Micromechanical study on the origin of fiber bridging under interlaminar and intralaminar mode I failure

Studies on Traction Separation Relations in Fracture of Layered Composites : Experiments and Modeling

Towards a geometry independent traction-separation and angle relation due to large scale bridging in DCB configuration

Individualized lightweight structures for biomedical applications using additive manufacturing and carbon fiber patched composites

Runaway electron beam control

The influence of through-thickness reinforcement geometry and pattern on delamination of fiber-reinforced composites: Part II - Modeling

Experiments and numerical modelling on angle-ply laminates under remote mode II loading

A comparative study of mode I delamination behavior of unidirectional glass fiber-reinforced polymers with epoxy and polyurethane matrices using two methods

The influence of through-thickness reinforcement geometry and pattern on delamination of fiber-reinforced composites: Part I - Experimental results

Variations on R-curves and traction-separation relations in DCB specimens loaded under end opening forces or pure moments

Monitoring of Torque Induced Strain in Composite Shafts with Embedded and Surface-Mounted Optical Fiber Bragg Gratings