Viscous liquid

In condensed matter physics and physical chemistry, the terms viscous liquid, supercooled liquid, and glass forming liquid are often used interchangeably to designate liquids that are at the same time highly viscous (see Viscosity of amorphous materials), can be or are supercooled, and able to form a glass. The mechanical properties of glass-forming liquids depend primarily on the viscosity. Therefore, the following working points are defined in terms of viscosity. The temperature is indicated for industrial soda lime glass: Fragility (glass physics) In a widespread classification, due to chemist Austen Angell, a glass-forming liquid is called strong if its viscosity approximately obeys an Arrhenius law (log η is linear in 1/T ). In the opposite case of clearly non-Arrhenius behaviour the liquid is called fragile. This classification has no direct relation with the common usage of the word "fragility" to mean brittleness. Viscous flow in amorphous materials is characterised by deviations from the Arrhenius-type behaviour: the activation energy of viscosity Q changes from a high value QH at low temperatures (in the glassy state) to a low value QL at high temperatures (in the liquid state). Amorphous materials are classified accordingly to the deviation from Arrhenius type behaviour of their viscosities as either strong when or fragile when QH-QL≥QL. The fragility of amorphous materials is numerically characterized by the Doremus’ fragility ratio RD=QH/QL . Strong melts are those with (RD-1) < 1, whereas fragile melts are those with (RD-1) ≥ 1. Fragility is related to materials bond breaking processes caused by thermal fluctuations. Bond breaking modifies the properties of an amorphous material so that the higher the concentration of broken bonds termed configurons the lower the viscosity. Materials with a higher enthalpy of configuron formation compared with their enthalpy of motion have a higher Doremus fragility ratio, conversely melts with a relatively lower enthalpy of configuron formation have a lower fragility.