Oxygen transport in La0.5Sr0.5Fe1-yTi yO3-δ (y=0.0,0.2) membranes

The influence of partial substitution of Fe with Ti on the oxygen transport properties of La1- xSrxFeO3 membranes was investigated in view of their application for oxygen separation. Samples of composition La0.5Sr0.5 Fe1-yTiyO3-δ (y = 0, 0.2) were prepared and their oxygen transport properties characterised by potential-step relaxation and by oxygen permeation measurement in an air/argon gradient. With the first technique, chemical diffusion (D) and surface exchange (kS) coefficients were obtained by fitting of the current relaxation data to a single expression valid over the complete time range. The Ti- substituted composition gave slightly larger values of D and kS. The trend was opposite for the measured oxygen permeation flux. In the latter experience, ordering of oxygen vacancies was observed at lower temperature, reducing significantly the performance of the material.

Chat with Graph Search

Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.

DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.

Oxygen transport in La0.5Sr0.5Fe1-yTi yO3-δ (y=0.0,0.2) membranes

Chat with Graph Search

Influence of micro-patterned support properties and interfacial polymerization conditions on performance of patterned thin-film composite membranes

From Surfactants to 3D Printing: How Ion-Chelator Pair Interactions Affect the Mechanical Properties of Bioinspired Materials

Functionalized Å-scale Pores in Graphene for Carbon Capture