DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
A central focus in high strain rate research is understanding the dynamic behavior of materials at strain rates where a strength upturn is observed. While strength upturns at strain rates of 10 3 to 10 4 s −1 have been widely reported in the literature, their occurrence in certain materials remains controversial, and the underlying physics driving this phenomenon is not yet fully understood. Current mechanical testing methods are limited, as no single technique spans the full strain rate range of 10 1 to 10 5 s −1 where this phenomenon is expected, and a unified technique would enable consistent post‐deformation characterization with minimal error. To address this, we developed a customized piezoelectric in situ nanomechanical test setup, enabling constant indentation strain rates up to 10 5 s −1 , for the first time. Using this system, we examined rate‐dependent hardness in single‐crystalline molybdenum, nanocrystalline nickel, and amorphous fused silica over strain rates from 10 1 to 10 5 s −1 , remarkably revealing a hardness upturn in all three materials. Further, post‐deformation analysis of single‐crystalline molybdenum revealed that the hardness upturn was primarily driven by increased dislocation density, with phonon drag—traditionally considered a dominant contributor playing a minimal role.