Publication

Sputtered silicon carbide thin films as protective coating for MEMS applications

Paul Muralt, Jacek Baborowski, Nicolas Ledermann
2000
Journal Articles

Abstract

There is a need for chemically resistant coatings that protect the exposed surface of microfluidics components. Pinhole free films with low stress and a good uniformity on flat and inclined surfaces are required. In this study, amorphous silicon carbide (SiC) thin films have been deposited by RF magnetron sputtering on hat surfaces and into micromachined cavities of Si (100). The variation of RF power, deposition pressure and substrate bias voltage have been studied. Depending on the deposition conditions, the film stress can be adjusted from - 1400 MPa to + 100 MPa. Modifications of the deposition rate and the morphology between normal and inclined (54.7 degrees) planes have been observed. Optimal chemical stability was found with slightly compressive (-100 MPa) SiC thin films. No degradation of the protective layer has been observed after 3 h in KOH at 80 degrees C. (C) 2000 Elsevier Science S.A. All rights reserved.

Official source

https://infoscience.epfl.ch/entities/publication/bc1bff08-9154-4da1-bcaa-427e02b82282

About this result

This page is automatically generated and may contain information that is not correct, complete, up-to-date, or relevant to your search query. The same applies to every other page on this website. Please make sure to verify the information with EPFL's official sources.

Graph Chat

Chat with Graph Search

Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.

DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.

Paul Muralt, Jacek Baborowski, Nicolas Ledermann
2000
Journal Articles

Abstract

Official source

https://infoscience.epfl.ch/entities/publication/bc1bff08-9154-4da1-bcaa-427e02b82282

About this result

Related concepts (32)

Physical vapor deposition

Physical vapor deposition (PVD), sometimes called physical vapor transport (PVT), describes a variety of vacuum deposition methods which can be used to produce thin films and coatings on substrates including metals, ceramics, glass, and polymers. PVD is characterized by a process in which the material transitions from a condensed phase to a vapor phase and then back to a thin film condensed phase. The most common PVD processes are sputtering and evaporation.

Chemical vapor deposition

Chemical vapor deposition (CVD) is a vacuum deposition method used to produce high-quality, and high-performance, solid materials. The process is often used in the semiconductor industry to produce thin films. In typical CVD, the wafer (substrate) is exposed to one or more volatile precursors, which react and/or decompose on the substrate surface to produce the desired deposit. Frequently, volatile by-products are also produced, which are removed by gas flow through the reaction chamber.

Electron-beam physical vapor deposition

Electron-beam physical vapor deposition, or EBPVD, is a form of physical vapor deposition in which a target anode is bombarded with an electron beam given off by a charged tungsten filament under high vacuum. The electron beam causes atoms from the target to transform into the gaseous phase. These atoms then precipitate into solid form, coating everything in the vacuum chamber (within line of sight) with a thin layer of the anode material.

Related publications (21)

Sputtered silicon carbide thin films as protective coating for MEMS applications

Chat with Graph Search

Atomic Layer Deposition of Copper using Cu(II) Hexafluoroacetylacetonate and Diethylzinc: Surface Reaction Mechanisms and Surface Material Selectivity

A 15-Year Record of Organic–Inorganic Phosphorus Variability in Eastern Mediterranean Wet Deposition

Adsorption-Driven Cloud Droplet Activation of Fresh and Aged Polypropylene Particles