DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
YMgNi4-based alloys exhibit reversible hydrogen absorption and desorption reactions at near room temperature. Here, we report that Co-substituted YMgNi4-based alloys exhibited higher hydrogen contents and lower hydrogen absorption and desorption reaction pressures than unsubstituted alloys. The effects of Co-substitution viewed from atomic arrangements were particularly clarified by synchrotron radiation powder X-ray diffraction, neutron diffraction, and inelastic neutron scattering. Powder neutron diffraction of the Co-substituted alloy at 5 MPa of D-2 pressure suggested the formation of gamma-phase deuteride (higher deuterium content) from beta-phase deuteride (lower deuterium content). However, no gamma-phase deuteride was observed in the unsubstituted alloys at 5 MPa. Therefore, the gamma-phase deuteride formation of the Co-substituted alloy at lower pressure led to higher hydrogen contents than the unsubstituted alloys. The combined results of powder neutron diffraction and inelastic neutron scattering suggested that the gamma-phase hydride of the Co-substituted alloy was continuously generated due to additional H atoms at the H atom sites in the beta-phase hydride because of the disordered H atomic arrangement involving H-H interactions. As a result, hydrogen absorption and desorption reaction pressures for the gamma-phase deuteride formation with higher hydrogen storage capacity were lowered.