Strain-based analysis on the influence of local undercut geometry on fatigue crack initiation life

Alain Nussbaumer, Heikki Tapani Remes, Abinab Niraula

The local undercut defects at the weld toe provide a potential initiation site for fatigue cracks and significantly impact the structure's fatigue strength. The influence of continuous undercut depth on fatigue performance is widely studied, but the resear ...

2024

Modeling friction and wear using an adaptive discrete-continuum coupling

Manon Eugénie Voisin--Leprince

When two objects slide against each other, wear and friction occur at their interface. The accumulation of wear forms what is commonly referred to as a ``third-body''. Understanding third-body evolution has significant applications in industry, where contr ...

EPFL2024

Tension-tension fatigue behavior of basalt composite hybrid joints

Thomas Keller, Lulu Liu, Xin Wang

The tension–tension fatigue behavior of pseudo-ductile hybrid bonded-bolted double lap basalt composite joints, composed of pseudo-ductile adhesives and adherends with multi-directional fiber architecture, was experimentally investigated. The fatigue damag ...

2024

Short-term behavior of glass fiber-polymer composite bending-active elastica beam under service load application

Thomas Keller, Landolf-Giosef-Anastasios Rhode-Barbarigos, Tara Habibi

Bending-active elastica beam is a structural configuration that is based on the elastic deformation of an initially straight beam. This deformation occurs when horizontal displacements are applied to a sliding support, causing the beam to bend into an arch ...

2024

Microscopic Digital Image Correlation Analysis of Strain Distributions in Stainless Steel 316L Induced by Multiaxial Cyclic Loading

Elif Cansu Kursun

Fatigue damage in materials results in localized strain at the microstructural level. In many engineering components of the cooling circuits of nuclear power plants, where austenitic steels are used, the material experiences multiaxial cyclic loading, eith ...

EPFL2023

Experimental testing and structural analysis of composite tile – reinforced concrete domes

Savvas Saloustros

Conventional formworks for concrete curved shells either are expensive, complex and wasteful or have formal restrictions. Using tile vaults (also known as timbrel, Guastavino, thin-tile or Catalan vaults) as stay-in-place formwork for concrete shells could ...

2023

Energy dissipation in fiber-polymer composites adhesive joints under cyclic loading

Ghazaleh Eslami

Sustainable development has emerged as a paramount consideration in various fields of industry, including construction, to preserve the environment and its finite resources. Lightweight structures, such as fiber-polymer composite structures, address both s ...

EPFL2023

Tree root distribution modelling in different environmental conditions

David Andrew Barry, Paolo Perona, Massimiliano Schwarz

The ability to predict the spatial distribution of tree root system variables (e.g., the Root system Area (RA), the maximum root diameter, the number of roots in diameter classes, the density of fine roots, etc.) under different environmental conditions is ...

2022

Understanding the mechanisms of adhesive wear for heterogeneous materials through atomistic simulations

Jean-François Molinari, Sacha Zenon Wattel, Antonio Joaquin Garcia Suarez

When two rough surfaces slide against each other, two main behaviors can be observed at the asperity level: A ductile behavior where the asperities tend to smooth out or a brittle behavior where the asperities detach and form debris. Recently, a critical l ...

2022

Probabilistic fatigue model for composites based on the statistical characteristics of the cycles to failure

Anastasios Vassilopoulos, Guangjian Xiang

A probabilistic model for estimating the fatigue life of composite laminates based on the mean value and standard deviation of the fatigue life is introduced here for predicting the distribution of fatigue life at any stress level for a constant stress rat ...

ELSEVIER SCI LTD2022

Cyclic Behaviour of Unidirectional Hybrid Interlayer Glass/Carbon and Carbon/Carbon Composites

Anastasios Vassilopoulos, José Manuel de Sena Cruz

The lack of ductility is a major drawback of fibre reinforced polymer (FRP) materials. As it is known, these materials are stiff and strong, but brittle with little or no warning before final failure. In the last decades, some solutions have been proposed ...

SPRINGER-VERLAG SINGAPORE PTE LTD2022

Crack propagation in CFRP laminates under mode I monotonic and fatigue loads: A methodological study

John Botsis, Charlie Joseph Simon Blondeau, Georgios Pappas

Delamination in composite materials is often accompanied by fiber bridging that increases resistance to crack growth. Here, delamination of two unidirectional carbon/epoxy systems was studied under monotonic and displacement-controlled fatigue loading. One ...

ELSEVIER SCI LTD2021

Fatigue examination of reinforced-concrete bridge slabs using acoustic emission and strain monitoring data

Imane Bayane

The examination of bridges under service loading is key for understanding their condition and thus for their sustainable and efficient use. The need to extend the service duration of existing bridges is increasing, and therefore, efficient tools for examin ...

EPFL2021

A novel fatigue life prediction methodology based on energy dissipation in viscoelastic materials

Thomas Keller, Ghazaleh Eslami

This paper introduces a new fatigue life prediction methodology for viscoelastic materials in the tension-tension fatigue loading region. The model was established based on the total amount of energy dissipated during fatigue loading, and offers two main a ...

ELSEVIER SCI LTD2021

Fatigue of reinforced UHPFRC members and monitoring of fatigue action effects on bridges

Bartlomiej Wojciech Sawicki

The objective of this thesis is to develop knowledge and methods to prevent fatigue failure of bridges. The Fatigue Limit State is investigated from both the demand (S) and resistance (R) side. The S-part focuses on reduction of uncertainties through monit ...

EPFL2021

Fatigue Performance of an Additively Manufactured Zr-Based Bulk Metallic Glass and the Effect of Post-Processing

Jamasp Jhabvala, Roland Logé, Navid Sohrabi, Milad Hamidi Nasab, Baptiste Thomas Jean Rouxel, Annapaola Parrilli

Fatigue is the most common cause of failure of mechanical parts in engineering applications. In the current work, we investigate the fatigue life of a bulk metallic (BMG) glass fabricated via additive manufacturing. Specimens fabricated via laser powder-be ...

MDPI2021

Multiaxial fatigue behavior and strengthening of riveted double-angle connections in steel bridges using prestressed CFRP rods

Hossein Heydarinouri

A large number of aging road and railway riveted metallic bridges suffer from fatigue problems. Stringer-to-floor-beam double-angle bridge connections are among the most fatigue-prone details due to the many cyclic distortion-induced stresses from axle loa ...

EPFL2021

Adhesive wear regimes on rough surfaces and interaction of micro-contacts

Jean-François Molinari, Son-Jonathan Pham-Ba

We develop an analytical model of adhesive wear between two unlubricated rough surfaces, forming micro-contacts under normal load. The model is based on an energy balance and a crack initiation criteria. We apply the model to the problem of self-affine rou ...

2021

Deformational behavior and damage mechanism of R-UHPFRC beam subjected to fatigue loading

Eugen Brühwiler, Bartlomiej Wojciech Sawicki, Antoine Bassil

The fatigue behavior of a reinforced UHPFRC (Ultra High Performance Fiber Reinforced Cementitious composite) T-shaped beam under four-point bending is investigated. The beam was subjected to a fatigue loading range equal to 49% of the static resistance and ...

2021

Origami-inspired carbon fiber-reinforced composite sandwich materials - Fabrication and mechanical behavior

Thomas Keller, Yuntong Du

A folding fabrication method inspired by origami for carbon fiber-reinforced composites to fabricate three-dimensional structures is presented. PMI foams serve as substrates, making it possible to manufacture this kind of origami-inspired composite sandwic ...

ELSEVIER SCI LTD2021