Deformational behavior and damage mechanism of R-UHPFRC beam subjected to fatigue loading

About
Privacy
Disclaimer

Graph Chatbot

Related publications (29)

Tension-tension fatigue behavior of basalt composite hybrid joints

The tension–tension fatigue behavior of pseudo-ductile hybrid bonded-bolted double lap basalt composite joints, composed of pseudo-ductile adhesives and adherends with multi-directional fiber architecture, was experimentally investigated. The fatigue damag ...

2024

Experimental and ab initio derivation of interface stress in nanomultilayered coatings: Application to immiscible Cu/W system with variable in-plane stress

Claudia Cancellieri, Pandula Manura Liyanage, Giacomo Lorenzin

Interface stress is a fundamental descriptor for interphase boundaries and is defined in strict relation to the interface energy. In nanomultilayers with their intrinsically high interface density, the functional properties are dictated by the interface st ...

Elsevier2024

An adaptive phase field approach to 3D internal crack growth in rocks

Tao Xu, Michael Heap, Alexandra Roma Larisa Kushnir

Modeling the 3D internal crack under compression entails complex fracture mechanics (mode I-II-III fracture), resulting in substantial computational costs and challenges in characterizing fracture morphology characterization for Phase Field Method (PFM) si ...

2024

A Softening Constitutive Law and Gradient-Inelastic Fiber-Based Element for 3-Dimensional Frame Simulations Under Seismic Excitations

Diego Isidoro Heredia Rosa

Steel frame structures are essential components of modern infrastructure. Understanding their behavior under seismic loading is critical for ensuring public safety and minimizing damage that occurs during earthquakes. To accurately predict the response of ...

EPFL2024

A pre-fatigue training strategy to stabilize LiCoO2 at high voltage

Lei Zhang, Rui Xia, Kangning Zhao

Layered cathodes are among the most promising cathodes for high-energy-density Li-ion batteries, yet hindered by the structural degradation from both bulk strain and surface oxygen loss at high voltage (above 4.5 V). Herein, we report a pre-fatigue trainin ...

Royal Soc Chemistry2024

Numerical investigation of two-dimensional Mode-II delamination in composite laminates

Thomas Keller, Anastasios Vassilopoulos, Congzhe Wang

Existing standards for delamination tests on composite materials typically employ one-dimensional (1D) beam specimens. However, such specimens may not represent real delamination scenarios in composite structures, where cracks tend to propagate in two dime ...

Elsevier Sci Ltd2024

FLO:RE – A new floor system made of reused reinforced concrete and steel elements

Maléna Bastien Masse, Numa Joy Bertola, Célia Marine Küpfer, Corentin Jean Dominique Fivet

Carefully extracting reinforced concrete (RC) elements from soon-to-be demolished structures and reusing them as load-bearing components is an emerging circular low-carbon alternative to building new structures. As floor construction typically accounts for ...

IABSE2024

Proliferation-driven mechanical compression induces signalling centre formation during mammalian organ development

Pengfei Xu, Sangwoo Kim

Localized sources of morphogens, called signalling centres, play a fundamental role in coordinating tissue growth and cell fate specification during organogenesis. However, how these signalling centres are established in tissues during embryonic developmen ...

Nature Portfolio2024

Multi-scale characterization and modeling of notched strength and translaminar fracture in hybrid thin-ply composites based on different carbon fiber grades

Guillaume Clément Broggi

Owing to their high specific stiffness and strength, Carbon Fiber Reinforced Composites (CFRP) are ideal candidates for the development of lightweight high-performance structures. Within this family, thin-ply composites allow for wider design freedom and p ...

EPFL2023