Fatigue Life Calculations in Metal Structures

In course

CIVIL-526: Steel structures, selected topics

Design and dimensioning of load-bearing structures using structural steel, with emphasis on the specific methods related to steel-concrete composite elements (for buildings and bridges), fatigue (bridges) and fire (buildings). ...

Description

This lecture covers the calculation of fatigue life in metal structures, including the parameters influencing lifespan, fracture mechanics, thickness effects in welded joints, and the stages of crack development. It also discusses the Manson-Coffin law, propagation laws, and the NASGRO law developed by NASA.

Instructor

Alain Nussbaumer

Official source

Related concepts (21)

Fracture mechanics

Fracture mechanics is the field of mechanics concerned with the study of the propagation of cracks in materials. It uses methods of analytical solid mechanics to calculate the driving force on a crack and those of experimental solid mechanics to characterize the material's resistance to fracture. Theoretically, the stress ahead of a sharp crack tip becomes infinite and cannot be used to describe the state around a crack. Fracture mechanics is used to characterise the loads on a crack, typically using a single parameter to describe the complete loading state at the crack tip.

Fracture

Fracture is the separation of an object or material into two or more pieces under the action of stress. The fracture of a solid usually occurs due to the development of certain displacement discontinuity surfaces within the solid. If a displacement develops perpendicular to the surface, it is called a normal tensile crack or simply a crack; if a displacement develops tangentially, it is called a shear crack, slip band or dislocation. Brittle fractures occur without any apparent deformation before fracture.

Fracture toughness

In materials science, fracture toughness is the critical stress intensity factor of a sharp crack where propagation of the crack suddenly becomes rapid and unlimited. A component's thickness affects the constraint conditions at the tip of a crack with thin components having plane stress conditions and thick components having plane strain conditions. Plane strain conditions give the lowest fracture toughness value which is a material property.

Fatigue (material)

In materials science, fatigue is the initiation and propagation of cracks in a material due to cyclic loading. Once a fatigue crack has initiated, it grows a small amount with each loading cycle, typically producing striations on some parts of the fracture surface. The crack will continue to grow until it reaches a critical size, which occurs when the stress intensity factor of the crack exceeds the fracture toughness of the material, producing rapid propagation and typically complete fracture of the structure.

Variable star

A variable star is a star whose brightness as seen from Earth (its apparent magnitude) changes with time. This variation may be caused by a change in emitted light or by something partly blocking the light, so variable stars are classified as either: Intrinsic variables, whose luminosity actually changes; for example, because the star periodically swells and shrinks. Extrinsic variables, whose apparent changes in brightness are due to changes in the amount of their light that can reach Earth; for example, because the star has an orbiting companion that sometimes eclipses it.

Related lectures (32)

Fatigue in Materials

Covers the concept of fatigue in materials, highlighting how repeated stress can lead to failure at lower levels than static rupture.

Materials Fatigue: Fracture and Toughness

Explores fatigue, fracture toughness, stress intensity, and crack propagation in materials.

Mechanical Tests: Creep and Fracture Mechanics

Explores creep tests, deformation, and fracture mechanics in mechanical tests.

Fracture Mechanics: Defects and Energy

Explores fracture mechanics, defects, stress factors, and energy release in material fracture.

Mechanical Properties of Materials: Toughness and Hardness