Lecture

Foundry Defects: Types and Solutions

Graph Chat

Chat with Graph Search

Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.

DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.

In course

ME-212: Mechanical Design I: Manufacturing Processes

Application des principales catégories de procédés de production. Modèles physiques élémentaires décrivant le comportement des principaux procédés de production. Compréhension de base des aspects économiques des procédés de production. Méthodologie de ...

Description

This lecture covers the different types of foundry defects such as unwelcome and cold drops, sink marks, cracks, pitting, blistering, and macro-segregation. It explains the causes of these defects and possible solutions to prevent them, including controlling filling pressure, adapting masselottage, and applying electromagnetic fields. The instructor also discusses the physico-chemical interactions between molds and parts, mold cracking, and mold erosion in sand foundries.

Instructor

Eric Boillat

Contact Microcity Phone: 41 21 69 54456 Teaching & PhD Past EPFL PhD Students as codirector Serguei Kolossov, Cédric André, Jamasp Jhabvala, Christoph Van Gestel, Tatiana Polivnikova, Nikola Kalentics Courses Industrial production processes ME-212 Application windows of the main manufacturing process categories. Implementation of simple models describing the behavior of the main manufacturing processes. Basic understanding of the economic aspects of production processes. Manufacturing proc

Official source

Related concepts (18)

Metal casting

In metalworking and jewelry making, casting is a process in which a liquid metal is delivered into a mold (usually by a crucible) that contains a negative impression (i.e., a three-dimensional negative image) of the intended shape. The metal is poured into the mold through a hollow channel called a sprue. The metal and mold are then cooled, and the metal part (the casting) is extracted. Casting is most often used for making complex shapes that would be difficult or uneconomical to make by other methods.

Sand casting

Sand casting, also known as sand molded casting, is a metal casting process characterized by using sand known as casting sand as the mold material. The term "sand casting" can also refer to an object produced via the sand casting process. Sand castings are produced in specialized factories called foundries. In 2003, over 60% of all metal castings were produced via sand casting. Molds made of sand are relatively cheap, and sufficiently refractory even for steel foundry use.

Casting defect

A casting defect is an undesired irregularity in a metal casting process. Some defects can be tolerated while others can be repaired, otherwise they must be eliminated. They are broken down into five main categories: gas porosity, shrinkage defects, mould material defects, pouring metal defects, and metallurgical defects. The terms "defect" and "" refer to two specific and separate things in castings. Defects are defined as conditions in a casting that must be corrected or removed, or the casting must be rejected.

Die casting

Die casting is a metal casting process that is characterized by forcing molten metal under high pressure into a mold cavity. The mold cavity is created using two hardened tool steel dies which have been machined into shape and work similarly to an injection mold during the process. Most die castings are made from non-ferrous metals, specifically zinc, copper, aluminium, magnesium, lead, pewter, and tin-based alloys. Depending on the type of metal being cast, a hot- or cold-chamber machine is used.

Electromagnetic field

An electromagnetic field (also EM field or EMF) is a classical (i.e. non-quantum) field produced by moving electric charges. It is the field described by classical electrodynamics (a classical field theory) and is the classical counterpart to the quantized electromagnetic field tensor in quantum electrodynamics (a quantum field theory). The electromagnetic field propagates at the speed of light (in fact, this field can be identified as light) and interacts with charges and currents.

Related lectures (64)

Casting & Molding: Physics of Manufacturing

Explores molding processes, casting physics, defects, key parameters, metal injection molding, and ongoing research on micro-/nano-scale casting.

Lost Wax Process and Croning Method

Covers the lost wax process and the Croning method for non-permanent molds.

Tooling and classification

Covers basic principles of various production processes and their classification.

Manufacturing Technologies: Forging, Casting and Molding

Explores forging, casting, and molding processes in manufacturing technologies, covering topics like extrusion, recrystallization, and metal injection molding.

Aluminum Alloys: Mechanical Properties and Processing Techniques