Concrete Durability: Corrosion and Degradation

In course

MSE-322: Building materials + Laboratory work

Science des matériaux de construction non métalliques les plus utilisés et plus particulièrement des matériaux cimentaires (béton). Composition chimique, fabrication et comportement sur la durée. ...

Description

This lecture covers the main causes of concrete degradation, including corrosion of reinforcements due to chlorides and carbonation. It explains the mechanisms of freeze-thaw degradation and alkali-aggregate reaction, along with prevention methods and laboratory tests. The instructor discusses exposure classes, diagnosis, and repair techniques for structures affected by corrosion and degradation.

This video is available exclusively on Mediaspace for a restricted audience. Please log in to MediaSpace to access it if you have the necessary permissions.

Watch on Mediaspace

Instructors (3)

Karen Scrivener

De nationalité anglaise, Karen Scrivener est née en 1958. Au cours de sa carrière, ses travaux et sa recherche traitaient des domaines suivants: Identification du développement microstucturale pendant l'hydratation du ciment. Elaboration d'une approche multitechnique pour étudier la microstucture des ciments et bétons, avec accent sur la quantification par analyse des images d'électrons retrodiffusés. Caractérisation de l'auréole de transition de la pâte de ciment autour des granulats. Compréhension des processus de dégardation des bétons, en particulier le gonflement lié à la formation de l'éttringite retardée dans les bétons étuvés.

Lionel Sofia

Emmanuelle Anne Boehm Courjault

Official source

Related concepts (32)

Corrosion

Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials (usually a metal) by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion. In the most common use of the word, this means electrochemical oxidation of metal in reaction with an oxidant such as oxygen, hydrogen or hydroxide. Rusting, the formation of iron oxides, is a well-known example of electrochemical corrosion.

Concrete

Concrete is a composite material composed of aggregate bonded together with a fluid cement that cures over time. Concrete is the second-most-used substance in the world after water, and is the most widely used building material. Its usage worldwide, ton for ton, is twice that of steel, wood, plastics, and aluminium combined. When aggregate is mixed with dry Portland cement and water, the mixture forms a fluid slurry that is easily poured and molded into shape.

Corrosion inhibitor

In chemistry, a corrosion inhibitor or anti-corrosive is a chemical compound that, when added to a liquid or gas, decreases the corrosion rate of a material, typically a metal or an alloy, that comes into contact with the fluid. The effectiveness of a corrosion inhibitor depends on fluid composition, quantity of water, and flow regime. Corrosion inhibitors are common in industry, and also found in over-the-counter products, typically in spray form in combination with a lubricant and sometimes a penetrating oil.

Corrosion engineering

Corrosion engineering is an engineering specialty that applies scientific, technical, engineering skills, and knowledge of natural laws and physical resources to design and implement materials, structures, devices, systems, and procedures to manage corrosion. From a holistic perspective, corrosion is the phenomenon of metals returning to the state they are found in nature. The driving force that causes metals to corrode is a consequence of their temporary existence in metallic form.

Galvanic corrosion

Galvanic corrosion (also called bimetallic corrosion or dissimilar metal corrosion) is an electrochemical process in which one metal corrodes preferentially when it is in electrical contact with another, in the presence of an electrolyte. A similar galvanic reaction is exploited in primary cells to generate a useful electrical voltage to power portable devices. This phenomenon is named after Italian physician Luigi Galvani (1737-1798).

Related lectures (35)

Concrete Durability: Carbonation and Chlorides

Explores concrete carbonation, reinforcement corrosion, prevention, and repair strategies, focusing on chlorides and freeze-thaw cycles.

Concrete Durability: Corrosion and Repair

Discusses concrete corrosion, freeze-thaw impact, alkali reaction, and acid attacks.

Carbonation of Concrete Structures MOOC: Sorption and transport in cementitious materials

Covers carbonation process, corrosion rates, and impact on concrete structures.

Chloride Ingress and Corrosion MOOC: Sorption and transport in cementitious materials

Explores the impact of chloride ingress on concrete structures and the mechanisms involved in corrosion.

Chloride Ingress: Mechanisms and Corrosion in Concrete MOOC: Sorption and transport in cementitious materials